Influence of acid etching on shear strength of different glass ionomer cements

Aim: To assess the influence of dental etching on the shear strength of different glass ionomer cements. Methods: The crown of 60 bovine incisors was prepared to obtain a flat, smooth surface, were attached to a PVC tube and randomly divided into six groups: Group 1 – Riva Self Cure without etching; Group II – Riva Self Cure with pre-etching; Group III – Maxxion R without etching; Group IV – Maxxion R with pre-etching; Group V – Ketac™Molar Easymix without etching; and Group VI – Ketac™Molar Easymix with pre-etching. Etching was performed with 10% polyacrylic acid for 30 s. A standardizing device was used for preparation of the test specimens (SBS Test Method). Following preparation, the specimens were stored in distilled water at 37º Cfor 24 h. The shear test was performed on a Kratos universal testing machine at a crosshead speed of 0.5 mm/min. The specimens were then viewed under a stereomicroscope at a magnification of x90 for analysis of fractures. Results: The results revealed that pre-etching increased the shear strength of Riva glass ionomer cement (SDI) alone, where as no statistically significant differences were found with regard to the other materials tested. Conclusions: Pre-etching with 10% polyacrylic acid for 30 s increased the shear strength of Riva glass ionomer cement.

Compressive strength of glass ionomer cements used for atraumatic restorative treatment / Resistência à compressão de cimentos de ionômero de vidro utilizados no tratamento restaurador atraumático

Purpose: This study evaluated the compressive strength of five glass ionomer cements (Ketac Molar, Fuji IX, Magic Glass, Vidrion R, and Vitro Molar) as a function of storage period (1 hour and 24 hours). Methods: Sixteen specimens of each material were fabricated according to ISO/DP #7489 Specification using a 6x12 mm (diameter and height) matrix. After setting, specimens were stored in distilled water at 37 ºC. Eight specimens per cement were subjected to the compressive strength test in a universal testing machine after 1 hour, and the other eight specimens were tested after 24 hours. Data were analyzed by ANOVA and Tukey's test (α=5%). Results: The compressive strength mean values (kgf) after 1 and 24 hours were: Ketac Molar: 218.75 and 297.88; Fuji IX: 335.75 and 350.88; Magic Glass: 61.50 and 140.13; Vidrion R: 142.38 and 230.88; and Vitro Molar: 183.38 and 297.50. After 1 hour Fuji IX had the highest compressive strength. All materials but Fuji IX showed higher compressive strength in 24 hours than in 1 hour. After 24 hours, no significant differences were found among Fuji IX, Ketac Molar, and Vitro Molar. Magic Glass had the lowest compressive strength in both storage periods. Conclusion: Fuji IX showed the best results after 1 hour. After 24-hour storage, Fuji IX, Ketac Molar, and Vitro Molar had similar performance.

Objetivo: Este estudo avaliou a resistência à compressão de 5 cimentos de ionômero de vidro (Ketac Molar, Fuji IX, Vitro Molar, Magic Glass e Vidrion R), em dois tempos de armazenagem (1 h e 24 h). Metodologia: Foram confeccionados 16 corpos-de-prova (CP) para cada material (n=8), seguindo as especificações da ISO/DP 7489. Os materiais foram manipulados e inseridos numa matriz desmontável (6 mm de diâmetro e 12 mm de altura). Após a presa os CP foram armazenados em água destilada a 37 ºC. Metade dos CP de cada material foi submetida a ensaio de compressão após 1 h e a outra metade foi testada após 24 h. Os resultados foram analisados por ANOVA e teste de Tukey (α=5%). Resultados: Os valores médios de resistência à compressão (kgf) após 1 h e 24 h foram: Ketac Molar: 218,75 e 297,88; Fuji IX:335,75 e 350,88; Magic Glass:61,50 e 140,13; Vidrion R:142,38 e 230,88, e Vitro Molar:183,38 e 297,50. Em 1 h o Fuji IX apresentou a maior resistência à compressão. Com exceção do Fuji IX, todos os ionômeros apresentaram maior resistência em 24h do que em 1 h. Em 24 h não houve diferença entre Fuji IX, Ketac Molar e Vitro Molar. O cimento Magic Glass apresentou os menores valores nos 2 tempos. Conclusão: O cimento Fuji IX apresentou os melhores resultados após 1 h. Após 24 h de armazenamento, Fuji IX, Ketac Molar e Vitro Molar tiveram desempenho similar.

Abfraction lesions reviewed: current concepts / Uma revisão sobre lesões de abfração: conceitos atuais

Non-carious cervical lesions are characterized by structural loss near the cementoenamel junction, without the presence of caries. A number of theories have arisen to explain the etiology of such lesions, although the real causes remain obscure, as is reflected by the contradictory terminology used in the literature. In addition to describing acidic and abrasive processes documented as etiological factors, attention is given to the role of mechanical stress from occlusal load, which is the most accepted theory for the development of abfraction lesions. Considering that tensile stress leads to the failure of restorations in the cervical region and that this is a fruitful area for future research, the present study has highlighted diagnosis, prognosis and the criteria for treatment.

As lesões cervicais não cariosas são caracterizadas pela perda de estrutura próxima à junção cemento-esmalte sem a presença de cárie. Algumas teorias têm surgido para tentar explicar a etiologia dessas lesões, embora as causas verdadeiras permaneçam obscura devido à terminologia contraditória na literatura. Apesar dos processos abrasivos e erosivos serem apontados como fatores etiológicos, atenção é dada ao papel da força biomecânica das cargas oclusais que é a teoria mais aceita para o desenvolvimento das lesões de abfração. Ao considerar que falhas de restauração podem ocorrer por tensões de tração e que constituem área promissora para pesquisas futuras, o presente trabalho demonstra os conceitos atuais sobre diagnóstico, prognóstico e critérios para o tratamento.

Avaliação in vitro da microinfiltração e adaptação marginal em restaurações classe V simulando lesões de abfração: estudo piloto / In vitro assessment of microleakage and marginal adaptation of class V restorations simulating abfraction lesions: a pilot study

Este estudo in vitro avaliou restaurações classe V, simulando lesões de abfração, quanto à microinfiltração e adaptação marginal. Vinte e quatro pré-molares superiores foram divididos em seis grupos(n=4), variando a combinação restauradora: G1=Ketac Molar Liquid/Ketac Molar Easymix, G2=Primer/Vitremer, G3=Adper Single Bond2/Durafill VS, G4=Adper Single Bond2/Z100, G5=Clearfil SE Bond/Durafill VS, G6=Clearfil SE Bond/Z100. Todos os dentes foram submetidos aos ensaios de ciclagem térmica(1000 ciclos/5º-55ºC), ciclagem mecânica (100.000 ciclos/8Kgf) e, em seguida, imersos em solução aquosade azul de metileno 0,5% (pH 7,2) por 4h. Os espécimes foram seccionados longitudinal e transversalmente, obtendo-se duas partes. A qualidade do selamento marginal foi avaliada através de dois métodos, um qualitativo, por meio de escores, e outro quantitativo, por análise morfométrica usando o software Imagelab 2000. Os resultados tratados pelos testes ANOVA a dois critérios e Tukey (5%) mostraram diferença estatística significativa (p < 0,05) em ambos os métodos, revelando menores valores de microinfiltração das restaurações para G1 e G2. Não houve diferença estatisticamente significante para a adaptação marginal em todos os grupos. Concluiu-se que os cimentos de ionômero de vidro convencional e modificado por resina são os mais indicados para restaurações em áreas de abfração quando comparados aos outros materiais testados.

Estudo comparativo da efetividade de selamento marginal de dois sistemas adesivos aplicados após a utilização de um material provisório a base de óxido de zinco e eugenol / Comparative study of marginal sealing effectiveness of two adhesive systems applied after using a zinc-oxide eugenol-based provisional material

O objetivo deste trabalho foi avaliar a influência de restaurações temporárias de óxido de de zinco eugenol (OZE) na microinfiltração marginal de restaurações de resina composta em esmalte e cemento-dentina, utilizando dois sistemas adesivos. Foram realizadas duas cavidades classe V padronizadas (3 X 3 X 2 mm) em quarenta molares humanos extraídos. Os dentes foram divididos em dois grupos: teste e controle. As cavidades do grupo-teste receberam restaurações provisórias com OZE e foram armazenadas por cinco dias em ambiente com umidade de 100 por cento. Os dentes do grupo de controle foram armazenadas nas mesmas condições do grupo-teste sem o OZE. O material foi removido com cureta e para cada dente dos grupos-teste e de controle uma das cavidades foi restaurada empregando-se um adesivo com condicionamento ácido total (Single Bond) e, na outra, um adesivo com primer autocondicionante (Cleartil SE Bond). A resina composta Filtek foi utilizada para restaurar as cavidades. Posteriormente à termociclagem, os dentes foram corados com azul de metileno (0,5 por cento)por 2h. Após lavados e secos, os espécimes foram cortados longitudinalmente e avaliados em lupa (40X), sendo os dados analisados estatisticamente pelo teste de Kruskal-Wallis. Em cemento-dentina observou-se que o OZE influenciou apenas o adesivo com primer autcondicionante e o Single Bond apresentou menor microinfiltração que o Clearfil tanto nos grupos com quanto naqueles sem OZE. Em esamlte não houve diferença estatísitica entre os grupos com e sem OZE quando utilizado o Clearfil. Este mostrou menor índice de microinfiltração em esmalte quando comparado ao Single Bond no grupo sem OZE e não houve diferença significativa em relação ao grupo com OZE.

Avaliação da microinfiltração da evolução de um sistema adesivo / Microleakage evaluation of a new adhesive system

O objetivo deste trabalho é avaliar a microinfiltração em cavidades classe II restauradas com os seguintes adesivos: Optibond Soloó (Sybron/Kerr) e Optibond Solo Plusó (Sybron/Kerr) associados à resina composta Prodigy Ó (Sybron/Kerr). Para isto, foram selecionados 8 pré-molares humanos hígidos, que receberam 16 cavidades envolvendo as superfícies mesial e distal, seguindo as seguintes dimensões: 4mm de largura, 2mm de profundidade e 6 mm de altura. Os sistemas adesivos foram aplicados de acordo com as instruções do fabricante e as cavidades foram preenchidas em 6 camadas de resina composta de aproximadamente I mm, sendo cada uma fotopolimerizada por 40 segundos (QHL 75 Curing Liteó - Dentisply). Posteriormente, as restaurações foram submetidas a termociclagem por 700 ciclos alternados entre 5 e 55° C e depois foram impermeabilizadas. Após a impermeabilização, os dentes permaneceram em solução de azul de metileno a 0,5% por 4 horas. Já corados, os dentes foram seccionados no sentido mesio-distal e então os fragmentos foram analisados quanto ao grau de microinfiltração através de escores. Obtidos os escores, estes foram submetidos ao teste não paramétrico de Kruskal-Wallis. Através da observação dos resultados podemos concluir que: os adesivos apresentaram melhor resistência quando utilizados em esmalte do que em dentina e não houve nenhuma diferença entre a ação dos sistemas adesivos utilizados...

Ligas para restaurações metalocerâmicas: uma revisão da literatura / Alloys for metalloceramic restorations: literature review

Durante muitos anos, as ligas nobres foram utilizadas como única alternativa para a confecção de restaurações metalocerâmicas e próteses parciais fixas. Posteriormente, o desenvolvimento de ligas básicas proporcionou um maior número de opções, com custo mais acessivel. Muitas são as ligas capazes de estabelecer união com cerâmicas odontológicas, diferindo quanto à manipulação e ao desempenho devido a variações na composição. As ligas nobres, apesar de seu excelente desempenho, perderam espaço em razão do seu alto custo; as ligas básicas por outro lado, apresentam como desvantagem problemas relacionados ao potencial alergênico de certos constituintes. Em virtude das excelentes propriedades mecânicas e de sua biocompatibilidade, o titânio surgiu como alternativa ao alto custo de ligas nobres e à sensibilidade das ligas básicas. Porém, há ainda problemas relacionados à técnica da fundição e união à porcelana, qua fazem necessárias várias pesquisas para torná-lo uma opção viável. Nesta revisão da literatura propõe-se discutir as ligas ondontológicas nobres e de metais básicos mais utilizadas para a confecção de restaurações metalocerâmicas em relação à composição e propriedades mecânicas, abordando também seus mecanismos de união com as porcelanas

Cimentaçäo de restauraçöes totalmente cerâmicas / Luting procedure of all-ceramic restorations

A longevidade de restauraçöes totalmente cerâmicas depende em grande parte da etapa de cimentaçäo. A cimentaçäo adesiva desse tipo de restauraçäo inclui os seguintes aspectos: a) a uniäo do adesivo ao substrato dental, b) o tratamento da superfície interna da peça, e c) as propriedades do cimento resinoso. A observaçäo de alguns cuidados relacionados a cada um desses fatores pode reduzir consideravelmente o risco de sensibilidade pós-operatória, descoloraçäo marginal, cárie secundária, descolamento ou fratura da peça. Este trabalho tem como objetivo apresentar as etapas clínicas da cimentaçäo de uma peça de porcelana feldspática

Avaliaçäo in vitro da infiltraçäo marginal em molares decíduos restaurados com resina composta modificada por poliácido, utilizando-se duas técnicas restauradoras / In vitro evaluation of marginal leakage in primary molars restored with polyacid-modified composite resin using two different techniques

O objetivo deste estudo foi de avaliar in vitro a infiltraçäo marginal em restauraçöes classe II de molares decíduos restaurados com uma resina composta modificada por poliácido (Dyract - Dentsply), utilizando-se duas diferentes técnicas restauradoras. Foram selecionados 10 segundos molares decíduos superiores, clinicamente hígidos, esfoliados naturalmente, onde foram confeccionados preparos cavitários do tipo "slot" vertical nas faces mesial e distal. No Grupo 1 seguiu-se as recomendaçöes do fabricante (aplicaçäo do sistema adesivo Dyract PSA - Dentsply), sem o prévio condicionamento ácido. No Grupo 2 utilizou-se um sistema adesivo (Scotchbond Multi-Uso Plus - 3M) com condicionamento ácido previamente à aplicaçäo do material restaurador. O Dyract foi levado aos preparos cavitários em 3 camadas incrementais seguidas da fotopolimerizaçäo. As amostras sofreram ciclagem térmica (700 ciclos - 5ºC e 55ºC), foram impermeabilizadas na regiäo radicular e receberam aplicaçäo de 2 camadas de esmalte de unha, deixando-se uma "janela" de aproximadamente 1 mm na margem cervical da restauraçäo. A seguir foram imersas em soluçäo de azul de metileno a 0,5 por cento durante 4 horas...

Estudo in vitro da influência do condicionamento ácido e da superfície, em dentina de dentes decíduos, na resistência de uniäo de resina composta e na micromorfologia dessa dentina condicionada / In vitro effect of type and time of etching of deciduous teeth dentin on tensile bond strength of composite and on dentine micromorphology

A pesquisa teve a finalidade de avaliar in vitro a resistência de uniäo, por ensaio de traçäo, empregando o sistema adesivo Scotchbond Multi-Purpose Plus e o compósito Z100, e a micromorfologia, pelo emprego do MEV, em dentina de dentes decíduos. Os fatores estudados foram: ácidos fosfórico, a 35 por cento (P35) e 10 por cento (P10), e maléico, a 10 por cento (M10), ou suas ausências; tempo de condicionamento ácido, de 5 e 15 segundos; superfícies de ensaio, vestibular e oclusal. Os resultados permitiram concluir que: sem condicionamento, a retentividade foi muito baixa; o P10 apresentou a maior retentividade com o condicionmento de 15 segundos; P35 com 5 segundos de condicionamento, apresentou baixa retentividade; em média as superfícies apresentaram retentividades semelhantes, mas que dependem do tempo e do ácido; o padräo de condicionamento ácido parece näo apresentar relaçäo confiável com a resistência de uniäo

Avaliaçäo da capacidade de retençäo de braquetes cerâmicos e metálicos colados em ambiente úmido / Evaluation of retention capacity of metallic and ceramic brackets bonded in wet environment

Objetivamos neste estudo avaliar a capacidade de retençäo, por meio de testes de traçäo, de braquetes metálicos com malha nas bases (Abzil-Lancer), braquetes metálicos com sulcos retentivos nas bases (Dyna-Lock) e cerâmicos policristalinos com retençäo mecânica nas bases (Clarity), colados em pré-molares humanos com o adesivo Transbond-XT associado ao agente adesivo hidrófilo Transbond-MIP ou com o cimento resinoso modificado fotopolimerizável de ionômero de vidro Fuji Ortho LC com e sem condicionamento ácido, ambos em ambiente úmido, comparando-os com o adesivo concise ortodontico, em ambiente seco. Os locais das falhas foram observados com microscopia ótica e fraturas do esmalte com microscopia eletrônica de varredura. Os braquetes metálicos colados com o Transbond-XT associado ao Transbond-MIP, em ambiente úmido, ou com o concise ortodôntico, em ambiente seco apresentaram as maiores capacidades de retençäo, estatisticamente superiores aos demais braquetes e sobretudo ao Fuji Ortho LC em ambiente úmido com e sem condicionamento ácido, o qual näo providenciou diferenças entre os braquetes. Houve maior frequência de falhas na interface esmalte-adesivo nos braquetes metálicos com malha (Abzil-Lancer) com os três adesivos e nos três tipos de braquetes colados com o Fuji Ortho LC, e na interface braquete-adesivo nos braquetes cerâmicos e metálicos com sulcos colados com o adesivo concise ortodôntico ou com o Transbond-XT associado ao Transbond-MIP. Houve somente um caso de fratura do esmalte com um braquete metálico colado com o Fuji Ortho LC

O último congressão do milênio / The last big congress of millenium

Mais do que uma boa oportunidade para aprender, reciclar-se e interagir com outros profissionais da Saúde, o 19º CIOSP abrirá espaços para a reflexão acerca do futuro da Odontologia no Brasil e no mundo

Avaliação in vitro da microinfiltração de adesivos em molares decíduos / An in vitro microleakage evaluation of adhesives in primary molars

A presente pesquisa teve como objetivo avaliar a microinfiltração de adesivos em molares decíduos, tendo sido selecionados 30 dentes, subdivididos em 10 grupos, de acordo com o material e técnica restauradora. Foram utilizados como adesivos, One Step (Bisco), Syntac (Vivadent), Prime Bond 2.1 (Caulk Dentsply), Clearfil Liner Bond 2 (Kuraray J. Morita) e Scotchbond M. P. Plus (3M), sendo realizado ou não, condicionamento ácido prévio. Os espécimes foram submetidos à ciclagem térmica (700 ciclos, de 5-55º, 1 min), impermeabilizados com esmalte cosmético, imersos em azul de metileno 0,5 por cento por 4 horas e seccionados. Foi realizada observação por três examinadores calibrados, sob iluminação e uso de lupa, e utilizados escores de 0-4 para teste de microinfiltração, segundo a penetração do corante, agrupando-se os dados obtidos. Foram efetuadas as análises estatísticas através dos testes de Kruskal-Wallis e de Mann-Whitney para comparação entre as técnicas. Não houve diferença estatisticamente significante entre os diferentes adesivos empregados, entretanto, quando comparados os grupos com e sem condicionamento ácido prévio, foi observada diferença estatisticamente significante, com valores menores de infiltração verificados naqueles previamente condicionados

Influência dos tipos de polimerizaçäo na resistência transversal da resina para base de prótese total / Influence of polymerization methods on flexural strength of denture base acrylic resins

O objetivo da pesquisa foi determinar a resistência transversal de resinas acrílicas para base de dentaduras ativadas química (RAAQ) e termicamente (RAAT). A polimerizaçäo da RAAQ foi feita com ativaçäo química apenas ou adicionalmente com térmica (1,5 h/70ºC + 1,0 h/100ºC). A polimerizaçäo da RAAT, por sua vez, foi realizada pelos métodos: usual (1,5 h/70ºC + 1,0 h/100ºC), com microondas e com luz de lâmpada halógena. Ainda, empregou-se uma resina de ativaçäo térmica especial, com um ciclo rápido (levar o banho até 100ºC, desligar a fonte de calor por 20 minutos, reaquecer até 100ºC e manter por 20 minutos). As conclusöes foram: a resistência transversal da RAAQ näo foi influenciada pelo método de polimerizaçäo; a resistência da RAAT tradicional também näo foi; o ciclo rápido conduziu a uma resistência muito baixa em relaçäo aos demais tipos, que näo foram significantes entre si

Avaliaçäo in vitro da infiltraçäo marginal nas cavidades proximais de molares decíduos restaurados com cimento de ionômero de vidro modificado por resina, utilizando-se dois diferentes procedimentos restauradores / In vitro evaluation of marginal leakage in primary molars restored with resin-modified glass ionomer cement using two different restorative procedures

Neste estudo foi realizado uma avaliaçäo in vitro da infiltraçäo marginal em cavidades classe II de molares decíduos, restaurados com cimento de ionômero de vidro modificado por resina (Vitremer - 3M), conforme as instruçöes do fabricante ou associado a um sistema adesivo (Scotchbond Multi-Uso Plus - 3M). Após as restauraçöes, as amostras foram submetidas ao processo de ciclagem térmica (5-55ºC/700 ciclos), imersos em soluçäo de azul de metileno, cortados e avaliados por cinco examinadores, os quais estabeceram o grau de infiltraçäo. Os dados foram analisados estatisticamente e revelaram que näo houve diferença significativa entre os dois diferentes tratamentos dados à superfície dos preparos cavitários antes da inserçäo do material restaurador quanto ao grau de penetraçäo do traçador utilizado

Influência do ajuste adicional na adaptaçäo de blocos fundidos tipo coroa/classe I / Influence of additional milling on the accuracy of crown/class I castings

A pesquisa teve por objetivo avaliar os ajustes de blocos fundidos de liga de níquel-cromo, constituídos por luvas cônicas, em que a parte interna representava uma coroa, e a externa, uma classe I. As fundiçöes foram feitas pelo método convencional, usando ou näo o alívio do troquel e o amianto. O anel era de plástico (PVC) flexível. Os corpos-de-prova que ainda näo tivessem se ajustado após a fase de bruto de fusäo eram jateados e, posteriormente, se ainda necessário, desgastados com brocas, para se chegar ao ajuste adequado. Ainda se verificou a influência da posiçäo dos blocos dentro do anel de fundiçäo (esquerda, central e direita) em relaçäo ao sentido de rotaçäo da centrífuga. Os resultados permitiram concluir que: a posiçäo dos blocos no anel de fundiçäo näo influiu nos ajustes dos mesmos; a influência da tira de amianto mostrou que o anel flexível de PVC näo a dispensa; o uso concomitante de alívio e tira de amianto conduziu a um número alto de coroas que se ajustavam adequadamente; o uso de tira de amianto aumenta a expressäo tanto de coroas como de classe I, e o alívio aumenta a de coroa e diminui a de classe I; sem o emprego de alívio, o jateamento e mesmo o uso de brocas se fazem necessários em alguns casos, para se conseguir um ajuste adequado

Avaliaçäo "in vitro" da infiltraçäo nas caixas próximas de pré-molares humanos restaurados com diferentes adesivos universais e resinas compostas / \"In vitro\" microleakage evaluation in proximal boxes restored with composite resins and hydrophilic bonding afentes

Neste trabalho avaliamos "in vitro" a infiltraçäo em restauraçöes feitas em duas resinas de características estruturais diferentes (micropartículas e ultrafinas) e associadas com três adesivos modernos de características hidrofílicas, aplicando-os sobre a superfície dentinária seca e úmida. Após a restauraçäo, os dentes foram imersos em água destilada a 37ºC por uma semana, sendo que alguns grupos sofreram novo condicionamento ácido com aplicaçäo de uma resina fluida (Fortify) na interface dente/restauraçäo. Em seguida, submetidos a ciclagem térmica (5/55ºC/700 ciclos) e mecânica (8,0Kgf/100.000 ciclos), imersos em soluçäo de nitrato de prata a 50 por cento, cortados e revelados sob luz intensa. Três avaliadores estabeleceram o grau de infiltraçäo (0 a 4) e os resultados analisados estatisticamente. A resina de micropartículas apresentou maior valor de infiltraçäo nos preparos em dentina e, também, em relaçäo a resina de partículas ultrafinas. A aplicaçäo da resina fluida pós-restauraçäo reduziu significantemente a infiltraçäo em esmalte e dentina para as duas resinas. A manutençäo da umidade na superfície dentinária diminuiu a infiltraçäo para todos os adesivos na resina de partículas ultrafinas e em apenas um deles essa diminuiçäo ocorreu para as duas resinas

Avaliação clínica de restaurações de amálgama com alto teor de cobre: 7 anos de acompanhamento / Clinical performance of amalgam restorations with high copper content: 7 years of follow-up

Foi desenvolvido um estudo clínico de restaurações de amálgama por meio de um longo período de acompanhamento (7 anos). Duas composições comerciais de ligas para amálgama com alto teor de cobre foram usadas e a análise seguiu os padrões estabelecidos pelo U.S.P.H.S. (Serviço de Saúde Pública dos Estados Unidos)

Avaliaçäo do desempenho clínico de restauraçöes de amálgama: 2 anos de acompanhamento / Clinical performance evaluation of amalgam restoration: two year follow-up

Um estudo clínico longitudinal de restauraçöes de amálgama feitas com nove ligas comerciais, foi executado de acordo com os critérios estabelecidos pelo U.S.P.H.S.(Serviço de Saúde Pública dos Estados Unidos). Para algumas das composiçöes com alto teor de cobre, a integridade marginal observada foi bastante satisfatória. Das nove ligas analisadas, três composiçöes (A21, VRe LU) mostraram um desempenho clínico médio melhor do que as cinco restantes (A2, VIII, EII, DS e NO), tendo a composiçäo convencional (V) como referência